punching drilling aluminum oxide Ceramic Disc disk roundel
Reputation depends on quality, quality comes from Hard!
Alumina Ceramics:
Alumina Ceramic experimented with a domestic alloy steel containing a large amount of chromium. After wear-resistant experiments, it was found that this alloy was not wear-resistant, indicating that it could not make guns. So they recorded the results of the experiment and threw them into the corner. thing. One day a few months later, an assistant rushed to Blairley with a piece of shiny steel and said, "Sir, this is the alloy steel from Mr. Mullah that I found when I was cleaning the warehouse. You Do you experiment to see what special effect it has!" "Okay!" Breerley said happily, looking at the dazzling steel. The experimental results prove that it is a piece of stainless steel that is not afraid of acid, alkali and salt. This stainless steel was invented by a German mullah in 1912, however, the mullah did not know what purpose this stainless steel had. Blairley thought to himself: "This kind of non-wearing but corrosion-resistant steel can't be used to make guns. Can it be used for tableware?" He just did it and made stainless steel fruit knives, forks, spoons, and fruit plates. And folding knives, etc. Stainless steel is often divided into martensitic steel, ferritic steel, austenitic steel, austenitic-ferritic (duplex) stainless steel and precipitation hardening stainless steel according to the state of organization. In addition, it can be divided into: chromium stainless steel, chromium nickel stainless steel and chromium manganese nitrogen stainless steel. There is also special stainless steel "GB24511_2009_Stainless steel plate and steel belt for pressure equipment" for pressure vessels. Containing 15% to 30% chromium. Its corrosion resistance, toughness and weldability increase with the increase of chromium content, and its resistance to chloride stress corrosion is better than other types of stainless steel, which belong to this category are Cr17 Cr17Mo2Ti, Cr25, Cr25Mo3Ti, Cr28, etc. Because of its high chromium content, ferritic stainless steel has good corrosion resistance and oxidation resistance, but its mechanical properties and process properties are poor. It is mostly used for acid-resistant structures with little stress and as anti-oxidation steel. This type of steel can resist corrosion from the atmosphere, nitric acid and salt solutions, and has the characteristics of good high-temperature oxidation resistance and low thermal expansion coefficient. It is used in nitric acid and food factory equipment, and can also be used to make parts that work at high temperatures, such as gas turbine parts, etc. .
properties: High hardness, high strength, wear resistance, corrosion resistance, high temperacture (1600°), good thermal diffusivity, good insulativity, low cost etc.
Data Sheet↓
Color: White/Ivory Density: 3.9g/cm3 Alumina Content: 96% 99% 99.5% Gas permeability: 0 Water Absorption: 0 MONS' Hardness: 82 Vickers Hardness (Hv50): 15.7(1600) Gpa(Kg/mm²) Flexural Strength(20°C): 330Mpa Compressive Strength(20°C): 2000Mpa Fracture Toughness (20°C): 4 MPam1/2 Thermal Conductivity(20°C): 27.5W(m.K) Thermal Expansion Coefficient: 7.6 10-6/°C Thermal Shock Resistance: 200 △T°C
Maximum use temperature 1650°C
Dielectric Strength: ＞10 KV/mm
Dielectric Constant: 9.1er
Dielectric Loss Angle(1MHz): 0.0002-0.0003
Volume Resistivity(20°C): ＞1014Ω.cm
Application industry: Machinery, electronic, chemical, petroleum etc. Specific application: Electrical ceramic substrate, plunger, sealing ring etc.
Why Choose Us? 1.12 years of professional production industrial ceramics factory 2.High quality products with low price 3.High precision parts with lowest tolerance 4.Short time for production 5.Has a group of experienced, professional and efficient R&D team 6.Has a good reputation in China and abroad. 7.MOQ is not limited, small quantity is welcome.
8.Vigorous team and good after-sales service
Products Show
FAQ
Q: Are you trading company or manufacturer ?
A: We are factory.
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is 15-30 days if the goods are not in stock, it is according to quantity.
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 50% T/T in advance ,balance before shippment.