isostatic pressing 3Y zirconia polished ceramic rod
Reputation depends on quality, quality comes from Hard!
Zirocnia Ceramics:
The Zirconia Ceramic Rod is processed by isostatic pressing process, and forms a uniform, fine and surface-lubricated ceramic layer and transition layer at high temperature and high speed. Because of the advanced manufacturing process, the cost is high, suitable for fine ceramic parts, and its wear resistance is more consolidated than other ceramic rods, generally used as a high wear-resistant place. The metallization of the Zirconia Ceramic rod is to adhere the ceramic rod to the inner wall of the metal with a high temperature resistant strong adhesive, and after solidification and solidification, a solid anti-wear layer is formed. The manufacturing process of this kind of product is relatively simple, the manufacturing cycle is short, and the cost is relatively low. Skill Standard: Mingrui Ceramics has ceramic rods of various scales, and can also be customized according to customer needs. Metallized ceramic rods are basically unconstrained by the size, and can be produced from 0.5mm to 160mm in diameter and even larger. The ceramic rod is punched with a high-temperature resistant adhesive to adhere the center holed ceramic rod to the inner wall of the metal, and the spot welding process is used to weld the ceramic to the inner wall of the steel sleeve through the small hole. To maintain the solder joint, screw the ceramic cap on top. Each porcelain rod is not only close to each other, but each of them constitutes a corresponding point of view, so that the porcelain rods are closely connected without gaps. When the last one of the laps is tightly embedded, the ceramic rods form a mechanical self-locking force of 360. The manufacturing process of the product is relatively messy, the manufacturing cycle is long, and the cost is high. The integrally formed wear-resistant ceramic rod is formed by firing all the ceramic rods and pouring them into the steel sleeve with special filling materials. The inner wall of the ceramic rod has good lubrication and sealing performance, and has excellent wear resistance and corrosion resistance.
Data Sheet↓
Color: Customized Density: 6.0g/cm3 Zirconia Content: 94.4% Gas permeability: 0 Water Absorption: 0 Crystal Size: 0.5um Rockwell Hardness(45N): 78R45N Vickers Hardness (Load 500g): 11.5(1175)Gpa(Kg/mm²) Flexural Strength(20°C): 800Mpa Compressive Strength(20°C): 2000Mpa
Modulus of Elasticity(20°C): ＞200Gpa
Fracture Toughness(20°C): 9.0 MPam1/2 Thermal Conductivity(20°C-400°C): 2.5W(m.K) Thermal Expansion Coefficient: 9.6 10-6/°C Thermal Shock Resistance: 250 △T°C
Application industry:
Machinery, fiber optic, knife, medical, food, petroleum etc.
Specific application:
plunger, Ceramic Shaft, fiber optic bushing, stub, grinding, ceramic knife, ceramic slide guide, machined plunger, mobile phone shell, watch case, haircut razor blade etc.
Why Choose Us? 1.12 years of professional production industrial ceramics factory 2.High quality products with low price 3.High precision parts with lowest tolerance 4.Short time for production 5.Has a group of experienced, professional and efficient R&D team 6.Has a good reputation in China and abroad. 7.MOQ is not limited, small quantity is welcome.
8.Vigorous team and good after-sales service
FAQ
Q: Are you trading company or manufacturer ?
A: We are factory.
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is 15-30 days if the goods are not in stock, it is according to quantity.
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 50% T/T in advance ,balance before shippment.