isolastic press forming zirconium oxide ceramics customized
Reputation depends on quality, quality comes from Hard!
Zirocnia Ceramics:
The production process of grouting is composed of the above nine processes, among which: the pulp is the process of adsorbing the moisture in the mud and forming the blank. The pulp is also called the empty pulp. When the blank forms a certain thickness, the excess mud is discharged. The process of returning the mud back to the slurry pool (or tank). The way of slurrying is: (1) artificial end barrel refining: (2) natural pressure re-pulping, using the slope of the pipeline to make the mud flow back to the mud pool; 3) Reclaiming the residual slurry by using the mud pump: (4) Negative pressure grouting, that is, using the bet-type pressure grouting pipeline, and using the negative pressure formed by the vacuum pump, pumping the mud back to the mud tank. In the above various modes, Except for the first type, it belongs to the pipeline back pulping. Consolidation: After the slurry is discharged, the blank is very soft. It cannot be demolded immediately. It takes a period of time to continue to remove the water and increase its strength. This time is called consolidation. Consolidation is a note. One of the main processes of slurry forming, the duration of which is about half of the time of the pulping. During the consolidation process, as the model continues to absorb water, the moisture content of the body continues to decrease, and the body gradually shrinks due to moisture drainage. When it drops to about 19-20% (ie, the demolding point), the consolidation process ends, and the blank is easily removed from the model. Take the mountain.
Data Sheet↓
Color: Customized Density: 6.0g/cm3 Zirconia Content: 94.4% Gas permeability: 0 Water Absorption: 0 Crystal Size: 0.5um Rockwell Hardness(45N): 78R45N Vickers Hardness (Load 500g): 11.5(1175)Gpa(Kg/mm²) Flexural Strength(20°C): 800Mpa Compressive Strength(20°C): 2000Mpa
Modulus of Elasticity(20°C): ＞200Gpa
Fracture Toughness(20°C): 9.0 MPam1/2 Thermal Conductivity(20°C-400°C): 2.5W(m.K) Thermal Expansion Coefficient: 9.6 10-6/°C Thermal Shock Resistance: 250 △T°C
Application industry:
Machinery, fiber optic, knife, medical, food, petroleum etc.
Specific application:
plunger, Ceramic Shaft, fiber optic bushing, stub, grinding, ceramic knife, ceramic slide guide, machined plunger, mobile phone shell, watch case, haircut razor blade etc.
Why Choose Us? 1.12 years of professional production industrial ceramics factory 2.High quality products with low price 3.High precision parts with lowest tolerance 4.Short time for production 5.Has a group of experienced, professional and efficient R&D team 6.Has a good reputation in China and abroad. 7.MOQ is not limited, small quantity is welcome.
8.Vigorous team and good after-sales service
FAQ
Q: Are you trading company or manufacturer ?
A: We are factory.
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is 15-30 days if the goods are not in stock, it is according to quantity.
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 50% T/T in advance ,balance before shippment.