low heat zirkonoxidkeramik hard ceramic ring spacer
Reputation depends on quality, quality comes from Hard!
Zirconia Ceramics:
Zirconia is a new important structural material used in the aerospace industry. Its specific gravity, strength and service temperature are between aluminum and steel, but it is stronger than aluminum and steel and has excellent seawater corrosion resistance and ultra-low temperature performance. In 1950, the United States used it for the first time on F-84 fighter-bombers as non-load-bearing components such as rear fuselage heat shields, wind deflectors, and tail covers. Since the 1960s, the use of titanium alloy moved from the rear fuselage to the middle fuselage, partially replacing structural steel to make important load-bearing components such as bulkheads, beams, and flap slides. The amount of titanium alloy used in military aircraft has increased rapidly, reaching 20% to 25% of the weight of the aircraft structure. Since the 1970s, civilian aircraft began to use titanium alloys in large quantities. For example, Boeing 747 passenger aircraft used more than 3,640 kilograms of titanium. Aircraft with a Mach number greater than 2.5 use titanium to replace steel to reduce structural weight. For another example, the US SR-71 high-altitude and high-speed reconnaissance aircraft (flying Mach number 3, flying height 26212 meters), titanium accounts for 93% of the weight of the aircraft structure, so-called "all-titanium" aircraft. When the thrust-to-weight ratio of the aero engine increases from 4-6 to 8-10, and the compressor outlet temperature increases from 200-300°C to 500-600°C, the original low-pressure compressor discs and blades made of aluminum must Zirconium oxide is used instead, or titanium alloy is used instead of stainless steel to make high-pressure compressor discs and blades to reduce structural weight.
Data Sheet↓
Color: Customized Density: 6.0g/cm3 Zirconia Content: 94.4% Gas permeability: 0 Water Absorption: 0 Crystal Size: 0.5um Rockwell Hardness(45N): 78R45N Vickers Hardness (Load 500g): 11.5(1175)Gpa(Kg/mm²) Flexural Strength(20°C): 800Mpa Compressive Strength(20°C): 2000Mpa
Modulus of Elasticity(20°C): >200Gpa
Fracture Toughness(20°C): 9.0 MPam1/2 Thermal Conductivity(20°C-400°C): 2.5W(m.K) Thermal Expansion Coefficient: 9.6 10-6/°C Thermal Shock Resistance: 250 △T°C
Application industry:
Machinery, fiber optic, knife, medical, food, petroleum etc.
Specific application:
Ceramic Plunger, Ceramic Shaft, fiber optic bushing, stub, grinding, ceramic knife, ceramic slide guide, machined plunger, mobile phone shell, watch case, haircut razor blade etc.
Why Choose Us? 1.12 years of professional production industrial ceramics factory 2.High quality products with low price 3.High precision parts with lowest tolerance 4.Short time for production 5.Has a group of experienced, professional and efficient R&D team 6.Has a good reputation in China and abroad. 7.MOQ is not limited, small quantity is welcome.
8.Vigorous team and good after-sales service
FAQ
Q: Are you trading company or manufacturer ?
A: We are factory.
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is 15-30 days if the goods are not in stock, it is according to quantity.
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 50% T/T in advance ,balance before shippment.